AFTER CASTING
| Yield strength (MPa) | > 500 |
| Elongation (%) | 14,61 |
| Young’s modul (GPa) | > 150 |
| Tensile strength (MPA) | 447 |
| density (g/cm³) | 8,4 |
| WAK / CTE (25 - 500°C) |
14,5 X 10¯⁶ K¯¹ |
| Hardness HV 10/30 | 310* |
dimensions (mm) (X) = 8 / 10 / 12,5 / 15 / 17,5 / 20 |
Ø 98,0 x (X) |
| Type acc. dIN EN ISO 22674 | ≥ type 4 as delivered |